HOPELEN FC-150B

About
HOPELEN FC-150B is a high melt flow rate (MFR) polypropylene homopolymer especially designed for metallizing cast film technology. The resin is specifically designed not to discolor and to provide excellent film optical properties. The resin has a high crystalline, a melting point of 165 °C and metallizing purpose. This material is available as an extruded pellet. This is a low smoke, low volatile resin. It contains an unusually low level of extractable.&&

About

HOPELEN FC-150B is a high melt flow rate (MFR) polypropylene homopolymer especially designed for metallizing cast film technology. The resin is specifically designed not to discolor and to provide excellent film optical properties. The resin has a high crystalline, a melting point of 165 °C and metallizing purpose. This material is available as an extruded pellet. This is a low smoke, low volatile resin. It contains an unusually low level of extractable.&&

Product Description
Supplier	LOTTE
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Low extract,Low smoke,High liquidity,Crystal,Optical performance,Low odor,Electroplating,Homopolymer
Availabilitys	North America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ASTM D792 , ISO 1183
Melt Flow Rate
230℃，2.16kg	8.0	g/10min	ASTM D1238，ISO 1133

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	25	J/m	ASTM D256，ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	115	℃	ASTM D648，ISO 75-2/B
Melting temperature	165	℃	Internal Method , ASTM D3418

optical performance	Nominal value	Unit	Test method
Haze
30 µ m, cast thin film	< 1.0	%	ASTM D1003

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	107		ASTM D785
R-level	107		ISO 2039-2
tensile strength
yield	35.3	MPa	ASTM D638 , ISO 527-2
Tensile strain
fracture	> 100	%	ASTM D638 , ISO 527-2
Bending modulus	1720	MPa	ASTM D790 , ISO 178
friction coefficient
Casting thin film	< 1.0		Internal Method

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.