| About |
|---|
| SFI-151 is the Homo polypropylene polymer manufactured by the Spheripol process. This grade is designed to potential end use applications include high transparency&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Weather resistance is good |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.0 | g/10min | ASTM D1238，ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 39 | J/m | ASTM D256 |
| 23℃ | 42 | J/m | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 113 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 80.0 | ℃ | ISO 75-2/B |
| Melting temperature | 162 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 30 µ m, cast thin film | < 2.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 102 | ASTM D785 | |
| R-level | 100 | ISO 2039-2 | |
| tensile strength | |||
| yield | 35.3 | MPa | ASTM D638 |
| yield | 32.4 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | |||
| — | 1470 | MPa | ASTM D790 |
| — | 1520 | MPa | ISO 178 |
| friction coefficient | |||
| Casting thin film | < 1.0 | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |