| About |
|---|
| 20% glass-fiber reinforced PC/ABS, easy mold release Non-brominated, non-chlorinated flame retardant Optimum combination of high modulus and impact strength&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Halogen free,Good stripping performance,Flame Characteristics,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.10 to 0.30 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 93.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 4.0 | % | ASTM D638 |
| Bending modulus | 5300 | MPa | ASTM D790 |
| bending strength | |||
| yield | 137 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 98 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 120 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 to 100 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 280 to 300 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 260 to 280 | °C | |
| Nozzle temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.39 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |