| About |
|---|
| PC/ABS with balanced flowability, impact properties and hydrolytic stability Non-brominated, non-chlorinated flame retardant&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Hydrolysis stability,Good liquidity,Halogen free,Flame Characteristics,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.40 to 0.60 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 57.9 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 100 | % | ASTM D638 |
| Bending modulus | 2450 | MPa | ASTM D790 |
| bending strength | |||
| yield | 86.3 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 490 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 80.0 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 240 to 260 | °C | |
| Barrel middle temperature | 230 to 250 | °C | |
| Barrel front temperature | 220 to 240 | °C | |
| Nozzle temperature | 240 to 260 | °C | |
| Processing (melt) temperature | 240 to 260 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.39 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |