| About |
|---|
| 高透光率，低雾度，紫外线稳定，中等粘度，高冲击强度。 |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Clarity,High impact resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 300℃，1.20kg | 15 | g/10min | ASTM D1238 |
| Density | 1.20 | ASTM D792 | |
| Shrinkage rate | 0.5 – 0.7 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 50 mm/min | 62 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 50 mm/min | >100 | % | ASTM D638 |
| bending strength | |||
| 10 mm/min | 92 | MPa | ASTM D790 |
| Bending modulus | 2400 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.86 MPa | 130 | ℃ | ASTM D648 |
| 0.45 MPa | 141 | ℃ | ASTM D648 |
| Vicat Softening Temp | 150 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 89 | % | ASTM D1003 |
| Haze | <0.8 | % | ASTM D1003 |
| Refractive index | 1.585 | ASTM D542 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 750 | J/M | ASTM D256 |
| Process Conditions | |||
|---|---|---|---|
| injection molding | Nominal value | Unit | Test method |
| Dry conditions | Nominal value | Unit | Test method |
| Melt temperature | 290 – 310 | °C | |
| Nozzle temperature | 280 – 300 | °C | |
| Barrel temperature, front section | 290 – 310 | °C | |
| Barrel temperature, middle section | 280 – 300 | °C | |
| Barrel temperature, rear section | 270 – 290 | °C | |
| Hopper temperature | 60 – 80 | °C | |
| Mold temperature | 60 – 90 | °C | |
| Drying temperature | 120 | °C | |
| Drying time | 4 | hrs | |
| Maximum water content | 0.02 | % | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |