| About |
|---|
| PC-1070U has higher viscosity, impact strength, tensile & flexural strength, and elastic modulus, which can be used in sheet-extrusion and stringent demand such as and goggles etc. Hopelex PC-1070U have UV stabilized ingredients to prevent degradation of final PC products from lights.&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,High impact resistance,High Viscosity,Good Tensile Strength |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 7.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 61.8 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 100 | % | ASTM D638 |
| Bending modulus | 2350 | MPa | ASTM D790 |
| bending strength | |||
| yield | 90.2 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 830 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 144 | ℃ | |
| 1.8 MPa, unannealed | 133 | ℃ | |
| Vicat Softening Temp | 153 | ℃ | ASTM D1525 5 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.585 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | < 0.80 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Barrel rear temperature | 290 to 310 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 270 to 290 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 290 to 310 | °C | |
| Mold temperature | 60.0 to 90.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.39 in/min |
| 4. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |