HOPELEX PCG-2200

About
20％玻纤增强，易脱模，高模量和冲击强度。

Product Description
Supplier	LOTTE
Generic	Polycarbonate
Material Status	Commercial: Active
Features	High impact resistance,Good stripping performance,Glass fiber reinforced,High modulus
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.33	g/cm³	ASTM D792
Shrinkage rate	0.2~0.4	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	103	MPa	ASTM D638
bending strength	167	MPa	ASTM D790
Bending modulus	4400	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	440	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa	140	℃	ASTM D648

Process Conditions
injection molding	Nominal value	Unit	Test method
Dry conditions	Nominal value	Unit	Test method
drying temperature	120	°C
Drying time	4	hrs
Maximum moisture content	0.02	%
Melt Temperature	300 – 320	°C
Nozzle temperature	290 – 310	°C
Barrel temperature, front section	280 ~ 300	°C
Barrel temperature, middle section	290 ~ 310	°C
Barrel temperature, rear section	300 – 320	°C
Hopper temperature	60 – 80	°C
Mold temperature	80 ~ 110	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.