| About |
|---|
| Easy Strippable Semiconductive Shielding E8413 is a crosslinkable easy-strippable semiconductive compound, designed for both XLPE and EPDM rubber insulated cables and use in both dry and steam curing processes. Specifications: E8413 meets the requirements as below, when optimal processing extrusion and end testing procedure are used: AEIC-CS 5/94 BS 6622 HN 33-S-23 (EDF) IEC 502 IEC 840 NF CS 32-223 SS 424 14 16, SS424 14 17 (HD 620 S1:1996) VDE 0273 / 12.87&& |
| Product Description | |
|---|---|
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Conductive,Good dissection,Steam Cure |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ASTM D1928 |
| Mooney viscosity | |||
| ML 1+4，121℃ | 21 | MU | ISO 289 |
| water content | < 800 | ppm | Internal Method |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength | |||
| 135℃，168 hr | -5.0 | % | ASTM D471 |
| Change rate of ultimate elongation | |||
| 135℃，168 hr | -50 | % | ASTM D471 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | |||
| 200℃ | 65/10 | % | IEC 60540 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | ASTM D257 | ||
| 23℃ | < 5.0E+2 | ohms·cm | ASTM D257 |
| 90 ℃ | < 1.0E+3 | ohms·cm | ASTM D257 |
| 120 ℃ | < 1.0E+3 | ohms·cm | ASTM D257 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Stripping Angle | 180 | ° | |
| Peeling force | |||
| EPR：23℃ | 1.5 to 2.0 | kN/m | |
| XLPE：23℃ | 1.0 to 1.5 | kN/m |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 85 to 90 | ASTM D2240 | |
| tensile strength | 11.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 260 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | < 40 | °C | |
| Barrel temperature | 23 | °C | |
| Barrel 1 zone temperature | 60 to 110 | °C | |
| Barrel 2 zone temperature | 60 to 110 | °C | |
| Barrel 3 zone temperature | 60 to 110 | °C | |
| Barrel 4 zone temperature | 60 to 110 | °C | |
| Barrel 5 zone temperature | 60 to 110 | °C | |
| Connector temperature | 100 to 130 | °C | |
| Nozzle temperature | 100 to 130 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. QAHC-10420 (Karl Fischer method) |
| 3. 20 N/cm² |
| 4. 50 mm/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |