| About |
|---|
| Hostacom EYS 2004L W92735 is an unfilled copolymer with high melt flow rate, high gloss, and high scratch resistance.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High liquidity,Copolymer,High scratch resistance |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 30 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 40.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 1700 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 32.0 | MPa | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 1700 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 0℃ | 2.0 | kJ/m² | |
| 23℃ | 3.0 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 0℃ | 70 | kJ/m² | |
| 23℃ | 90 | kJ/m² |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 89 | DIN 67530 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |