Hostacom G4 R01 BLACK

About
Hostacom G4 R01 BLACK is a 40% glass fiber reinforced PP homopolymer, with excellent stiffness, good dimensional stability, low creep under load at elevated temperatures and good LTHS (long term heat stability). It has been designed for parts in contact with copper and copper alloys. The product is available in black color, pellet form. This grade is not intended for medical, pharmaceutical, food and drinking water applications.&&

About

Hostacom G4 R01 BLACK is a 40% glass fiber reinforced PP homopolymer, with excellent stiffness, good dimensional stability, low creep under load at elevated temperatures and good LTHS (long term heat stability). It has been designed for parts in contact with copper and copper alloys. The product is available in black color, pellet form. This grade is not intended for medical, pharmaceutical, food and drinking water applications.&&

Product Description
Supplier	LyondellBasell
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,Good heat aging resistance,Good flexibility,Good Dimensional Stability,Homopolymer
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.21	g/cm³	ISO 1183/A
Melt Flow Rate
230℃，2.16kg	3.0	g/10min	ISO 1133
Melt Volume Rate
230℃，2.16 kg	3.00	cm³/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	9000	MPa	ISO 527-2
tensile strength
Yield, 23 ℃	110	MPa	ISO 527-2
Tensile strain
fracture	3.0	%	ISO 527-2
Bending modulus
23℃	8700	MPa	ISO 178-A
bending strength
23℃	150	MPa	ISO 178-A

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	8.5	kJ/m²	ISO 179/1eA
23℃	11	kJ/m²	ISO 179/1eA
Charpy Unnotch Impact strength
23℃	50	kJ/m²	ISO 179/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	160	℃	ISO 75-2/B
1.8 MPa, unannealed	147	℃	ISO 75-2/A
Vicat Softening Temp	135	℃	ISO 306/B

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.