| “Hostacom M4 N01 L255013 is a 40% mineral filled polypropylene homopolymer. The product is designed for injection molding of washing machine parts and is available in different white colors. UL listing in white and grey color. It is not intended for medical, pharmaceutical or drinking water applications.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Low liquidity,Homopolymer,Resistance to detergents,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，5.0kg | 11 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，5 kg | 11.0 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0℃ | 1.5 | kJ/m² | ISO 179/1eA |
| 23℃ | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| 0℃ | 15 | kJ/m² | ISO 179/1eU |
| 23℃ | 30 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 72.0 | ℃ | ISO 75-2/A |
| Relative temperature index | 65.0 | ℃ | UL 746 |
| Electrical performance | 65.0 | ℃ | UL 746 |
| Impact mechanical performance | 65.0 | ℃ | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 90.0 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| Secant | 3500 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 33.0 | MPa | ISO 527-2/50 |
| Tensile strain | ISO 527-2/50 | ||
| yield | 4.0 | % | ISO 527-2/50 |
| fracture | > 5.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| Secant | 3800 | MPa | ISO 178 |
| bending strength | |||
| 3.50% strain | 48.0 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |