| Hostacom M4 U02 NA BLACK is a 40% mineral filled PP homopolymer with high flow, high stiffness and low warpage. It is not intended for medical, pharmaceutical or drinking water applications.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,High liquidity,Homopolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 32.0 | MPa | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 4300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 2.0 | kJ/m² | ISO 180 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |