Hostacom TKC 2007N D12899 is a 5% talc filled PP copolymer, with low density, excellent blooming resistance at elevated temperatures, very good impact/stiffness balance, very good mouldability and excellent scratch resistance. Advanced technologies allowed for a significant reduction of mineral filler content which contributed to the reduction of final part weight. Please contact LyondellBasell for shrinkage recommendations. This product is also available in other colors, new colors can be developed depending on customer requirements.&&

About

Hostacom TKC 2007N D12899 is a 5% talc filled PP copolymer, with low density, excellent blooming resistance at elevated temperatures, very good impact/stiffness balance, very good mouldability and excellent scratch resistance. Advanced technologies allowed for a significant reduction of mineral filler content which contributed to the reduction of final part weight. Please contact LyondellBasell for shrinkage recommendations. This product is also available in other colors, new colors can be developed depending on customer requirements.&&

Product Description
Supplier	LyondellBasell
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,High impact resistance,Low to No Fogging,Low density,Copolymer,High scratch resistance
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.930	g/cm³	ISO 1183/A
Melt Flow Rate
230℃，2.16kg	16	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 23 ℃	20.0	MPa	ISO 527-2
Tensile strain
Yield, 23 ℃	4.8	%	ISO 527-2
Bending modulus
23℃	1650	MPa	ISO 178-A

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
-30℃	4.8	kJ/m²
23℃	35	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	56.0	℃	ISO 75-2/A
Vicat Softening Temp
A50	136	℃	ISO 306/A50

Notes
1. Typical properties: these are not to be construed as specifications.
2. 0.039 in/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.