| About |
|---|
| POM copolymer Easy flowing Injection molding type like C 13021, but with higher strength, rigidity and hardness over the entire permissible temperature range for HOSTAFORM; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. With UV Additives Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm. Ranges of applications: For molded parts with higher requirements to strength, rigidity und hardness, FMVSS = Federal Motor Vehicle Safety Standard (USA)&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Alkali resistant,Hydrolysis stability,Good liquidity,Solvent resistance,Fuel resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 12.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.8 | % | ISO 294-4 |
| MD | 2.0 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.65 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3050 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 68.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 8.0 | % | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | 20 | % | ISO 527-2/1A/50 |
| Tensile Creep Modulus（1 hr） | 2750 | MPa | ISO 899-1 |
| Tensile creep modulus | |||
| 1000 hr | 1450 | MPa | ISO 899-1 |
| Bending modulus | |||
| 23℃ | 3000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.7 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 120 | kJ/m² | ISO 179/1eU |
| 23℃ | 120 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 107 | ℃ | ISO 75-2/A |
| Melting temperature | 170 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 35 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 4.00 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 5.0E-3 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 to 140 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 170 to 180 | °C | |
| Barrel middle temperature | 180 to 190 | °C | |
| Barrel front temperature | 190 to 200 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Processing (melt) temperature | 190 to 210 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Injection pressure | 60.0 to 120 | MPa | |
| Injection speed | Slow-Moderate | ||
| Hold pressure | 60.0 to 120 | MPa | |
| Back pressure | 0.00 to 2.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 30s |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |