| Preliminary Data Sheet Hostaform® acetal copolymer grade LX90Z XAP2 TM is UV stabilized material available in a range of molded in metallic colors generally for automotive interior applications. In addition, Hostaform® LX90Z XAP2 TM has lower volatile emissions as required for some automotive interiors. Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application. Low Emission Performance [VDA-275] <5 PPM&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low odor |
| Availabilitys | North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 8.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.4 | % | ISO 294-4 |
| MD | 2.3 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.75 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2700 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 54.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 8.0 | % | ISO 527-2/1A/50 |
| Bending modulus | |||
| 23℃ | 2900 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 4.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 90.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 147 | ℃ | ISO 75-2/B |
| Melting temperature | 166 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 1.0E-4 | 1/℃ | ISO 11359-2 |
| MD | 9.0E-5 | 1/℃ | ISO 11359-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 105 to 110 | °C | |
| Drying time | 3.0 | hr | |
| Barrel rear temperature | 170 to 175 | °C | |
| Barrel middle temperature | 170 to 180 | °C | |
| Barrel front temperature | 175 to 185 | °C | |
| Nozzle temperature | 185 to 195 | °C | |
| Processing (melt) temperature | 180 to 195 | °C | |
| Mold temperature | 80 to 105 | °C | |
| Injection pressure | 60.0 to 120 | MPa | |
| Injection speed | Slow | ||
| Hold pressure | 60.0 to 120 | MPa | |
| Back pressure | 0.00 to 4.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |