| Chemical abbreviation according to ISO 1043-1: POM-HI Molding compound ISO 9988- POM-K, M-GNPR, 05-001 POM copolymer, modified Easy flowing, elastomer-containing injection molding type based on HOSTAFORM C 27021 with high toughness, and slightly lower hardness, rigidity and chemical resistance than the basic type; high resistance to thermal and oxidative degradation. UL-registration in natural and a thickness more than 1.57 mm as UL 94 HB. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm thickness. Ranges of applications: For thin-walled molded parts with high energy-absorbing capacity. UL = Underwriters Laboratories (USA) FMVSS = Federal Motor Vehicle Safety Standard (USA)&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Good liquidity,Ultra high toughness,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 18.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.7 | % | ISO 294-4 |
| MD | 1.8 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.65 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1700 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 44.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | 35 | % | ISO 527-2/1A/50 |
| Tensile creep modulus | ISO 899-1 | ||
| 1 hr | 1400 | MPa | ISO 899-1 |
| 1000 hr | 800 | MPa | ISO 899-1 |
| Bending modulus | |||
| 23℃ | 1700 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 110 | kJ/m² | ISO 179/1eU |
| 23 ℃, localized fracture | 150 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 77.0 | ℃ | ISO 75-2/A |
| Melting temperature | 166 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.3E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric strength | 28 | kV/mm | IEC 60243-1 |
| Relative permittivity | IEC 60250 | ||
| 100 Hz | 4.40 | IEC 60250 | |
| 1 MHz | 4.40 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 0.010 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.15 | % | |
| Hopper temperature | 20 to 30 | °C | |
| Barrel rear temperature | 170 to 180 | °C | |
| Barrel middle temperature | 180 to 190 | °C | |
| Barrel front temperature | 190 to 200 | °C | |
| Nozzle temperature | 190 to 200 | °C | |
| Processing (melt) temperature | 190 to 200 | °C | |
| Mold temperature | 60 to 70 | °C | |
| Injection pressure | 60.0 to 120 | MPa | |
| Injection speed | 慢to中等 | ||
| Hold pressure | 60.0 to 120 | MPa | |
| Back pressure | 0.00 to 2.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 30s |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |