Hostalen ACP 9255 Plus

About
Hostalen ACP 9255 Plus is a high density polyethylene resin which possesses an outstanding combination of stiffness and impact performance. Hostalen ACP 9255 Plus can be processed on blown film lines at high output rates with excellent bubble stability, very low gel levels and homogeneous appearance which converters and end-users require for high quality thin and thick film production. Hostalen ACP 9255 Plus can enable the production of films with a very broad conversion window, good lay flat properties and excellent roll configuration. Typical applications are lamination and release films, artificial paper, labels, bags and heavy duty packaging. This product is not intended for use in medical and pharmaceutical applications.&&

About

Hostalen ACP 9255 Plus is a high density polyethylene resin which possesses an outstanding combination of stiffness and impact performance. Hostalen ACP 9255 Plus can be processed on blown film lines at high output rates with excellent bubble stability, very low gel levels and homogeneous appearance which converters and end-users require for high quality thin and thick film production. Hostalen ACP 9255 Plus can enable the production of films with a very broad conversion window, good lay flat properties and excellent roll configuration. Typical applications are lamination and release films, artificial paper, labels, bags and heavy duty packaging. This product is not intended for use in medical and pharmaceutical applications.&&

Product Description
Supplier	LyondellBasell
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Good dissection,Low speed solidification point,Inoxidizability
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.957	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，21.6kg	12	g/10min	ISO 1133
190℃，5.0kg	0.40	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness	8 to 200 µm
tensile strength			ISO 527-3
MD, 20 µ m, blow molded film	75.0	MPa	ISO 527-3
TD, 20 µ m, blow molded film	65.0	MPa	ISO 527-3
Tensile strain			ISO 527-3
MD, fracture, 20 µ m, blow molded film	450	%	ISO 527-3
TD, fracture, 20 µ m, blow molded film	470	%	ISO 527-3
Drop hammer impact
20 µ m, blow molded film	> 200	g	ASTM D1709

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	200 to 230	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.