| Hostalen CRP 100 black is a high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 100 and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good heat aging resistance,High Viscosity,Good sensory characteristics.,Good wear resistance,High density,Solvent resistance,Welding,High ESCR |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，21.6kg | 6.4 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.23 | g/10min | ISO 1133 |
| Full incision creep test | |||
| 80℃ | > 1.4 | month | ISO 16770 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Maximum Elongation（TD） | > 350 | % | EN 638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 13 | kJ/m² | ISO 179 |
| 23℃ | 26 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 74.0 | ℃ | ISO 306 |
| Oxygen sensing time | |||
| 210℃ | 30 | min | ISO 11357-6 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| MRS Classification | 10.0 | MPa | ISO TR 9080 |
| Odor Threshold | < 2.00 | EN 1622/EN 1420 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3 seconds | 63 | ISO 868 | |
| Tensile modulus | |||
| Secant, 23 ℃ | 1100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 23.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 8.0 | % | ISO 527-2/50 |
| Tensile creep modulus | ISO 899-1 | ||
| 1 hr | 850 | MPa | ISO 899-1 |
| 1000 hr | 360 | MPa | ISO 899-1 |
| Bending creep modulus | DIN 19537-2 | ||
| 1 min | 1.20 | GPa | DIN 19537-2 |
| 2000 hr | 0.330 | GPa | DIN 19537-2 |
| 24 hr | 0.560 | GPa | DIN 19537-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 200 to 280 | °C | |
| Barrel middle temperature | 200 to 280 | °C | |
| Barrel front temperature | 200 to 280 | °C | |
| Processing (melt) temperature | 190 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4.0 MPa, 2% Arkopal N100 |
| 3. 2 MPa |
| 4. 4-point loading, 2000 hr |
| 5. 4-point loading, 1 min |
| 6. 4-point loading, 24 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |