| About |
|---|
| Hostalen CRP 100 RD black is a high density polyethylene. The new generation of PE100 material has been designed to meet new technical requirements for drinking water pipe systems. The material exibits an improved resistance against disinfectants. The material is black coloured similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 100 and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | High Viscosity,High ESCR |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，21.6kg | 6.4 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.23 | g/10min | ISO 1133 |
| Full incision creep test | |||
| 4 MPa，80℃ | > 1.4 | month | ISO 16770 |
| Carbon black content | 2.3 | % | ISO 6964 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 13 | kJ/m² | ISO 179 |
| 23℃ | 26 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 74.0 | ℃ | ISO 306 |
| Oxygen sensing time | |||
| 210℃ | 30 | min | ISO 11357-6 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| MRS Classification | 10.0 | MPa | ISO 9080 |
| Odor Threshold | < 2.00 | EN 1622/EN 1420 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3 seconds | 63 | ISO 868 | |
| Tensile modulus | |||
| Secant, 23 ℃ | 1100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 23.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃ | 8.0 | % | ISO 527-2/50 |
| fracture | > 350 | % | EN 638 |
| Tensile creep modulus | ISO 899-1 | ||
| 1 hr | 850 | MPa | ISO 899-1 |
| 1000 hr | 360 | MPa | ISO 899-1 |
| bending strength | |||
| 3.50% strain | 21.0 | MPa | ISO 178 |
| Bending creep modulus | DIN 19537-2 | ||
| 1 min | 1.20 | GPa | DIN 19537-2 |
| 2000 hr | 0.330 | GPa | DIN 19537-2 |
| 24 hr | 0.560 | GPa | DIN 19537-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 280 | °C | |
| Melt temperature | 190 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4.0 MPa, 2% Arkopal N100 |
| 3. 2 MPa |
| 4. 4-point loading, 2000 hr |
| 5. 4-point loading, 1 min |
| 6. 4-point loading, 24 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |