| About |
|---|
| Hostalen PP H5416 K is a natural nucleated polypropylene random copolymer. The product has a high heat- and extremely high extraction stability. It is not intended for medical and pharmaceutical applications.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Nucleation,High Heat Resistance,Inoxidizability,Random copolymer |
| Availabilitys | Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 , ASTM D1505 |
| Melt Flow Rate | ASTM D1238 , ISO 1133 | ||
| 190℃，5.0kg | 0.50 | g/10min | ASTM D1238，ISO 1133 |
| 230℃，2.16kg | 0.30 | g/10min | ASTM D1238，ISO 1133 |
| 230℃，5.0kg | 1.3 | g/10min | ASTM D1238，ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 800 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 26.5 | MPa | ASTM D638 |
| Yield, 23 ℃ | 24.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 10 | % | ASTM D638 |
| Yield, 23 ℃ | 10 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 834 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | ISO 179 | ||
| -20℃ | 45 | kJ/m² | ISO 179 |
| 0℃ | 无断裂 | ISO 179 | |
| 23℃ | 无断裂 | ISO 179 | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 230 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 83.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 65.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 123 | ℃ | ASTM D1525 |
| A50 | 125 | ℃ | ISO 306/A50 |
| Melting temperature | 141 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 1.5E-4 | 1/℃ | ISO 11359-2 |
| Thermal conductivity coefficient | 0.24 | W/m/K | ASTM C177 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+14 | ohms | ASTM D257，IEC 60093 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 280 | °C | |
| Melt temperature | 200 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min, 2nd heating |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |