Hostalen PP XN112-I

About
Hostalen PP XN112-I is a natural colored polypropylene random copolymer. The product Hostalen PP XN112-I has been classified through ISO9080 and according to ISO12162 as PP112. The regression curves of Hostalen PP XN112-I are above the reference lines of PP-RCT mentioned in DIN8077, DIN 8078 and EN ISO15874 standards for piping applications under pressure. Hostalen PP XN112-I is typically used by customers in the application pressure piping systems for hot and cold water. For further details about the suitable applications for this material please contact LyondellBasell.&&

About

Hostalen PP XN112-I is a natural colored polypropylene random copolymer. The product Hostalen PP XN112-I has been classified through ISO9080 and according to ISO12162 as PP112. The regression curves of Hostalen PP XN112-I are above the reference lines of PP-RCT mentioned in DIN8077, DIN 8078 and EN ISO15874 standards for piping applications under pressure. Hostalen PP XN112-I is typically used by customers in the application pressure piping systems for hot and cold water. For further details about the suitable applications for this material please contact LyondellBasell.&&

Product Description
Supplier	LyondellBasell
Generic	PP copolymer
Material Status	Commercial: Active
Features	Inoxidizability,Good sensory characteristics.,Random copolymer
Availabilitys	Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Flow Rate			ISO 1133
190℃，5.0kg	0.40	g/10min	ISO 1133
230℃，2.16kg	0.20	g/10min	ISO 1133
230℃，5.0kg	1.1	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	800	MPa	ISO 527-2
tensile strength
yield	24.0	MPa	ISO 527-2
Tensile strain
yield	32	%	ISO 527-2

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
0℃	9.5	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Melting temperature	135	℃	DSC

Supplementary information	Nominal value	Unit	Test method
MRS Classification	11.2	MPa	ISO 9080

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Processing (melt) temperature	230 to 280	°C
Melt temperature	230 to 240	°C
Calibration temperature, first time	35 to 40	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.