| Produce strong, ductile, functional parts Thermoplastic material delivering optimal mechanical properties. Renewable raw material from vegetable castor oil (reduced environmental impact). Provides excellent chemical resistance and enhanced elongation-at-break. Impact resistance and ductility for prostheses, insoles, sports goods, snap fits, living hinges, and more. Quality at the lowest cost per part Achieve the lowest cost per part1 and reduce your total cost of ownership. Minimize waste – reuse surplus powder batch after batch and get functional parts, no throwing away anymore. Get consistent performance while achieving 70% surplus powder reusability. Optimize cost and part quality – cost-efficient material with industry-leading surplus powder reusability. Engineered for HP Multi Jet Fusion technology Designed for production of functional and final parts across a variety of industries. Provides the best balance between performance and reusability. Easy-to-process material enables high productivity, less waste, and lower cost. Engineered to reliably produce final parts and functional prototypes with fine detail, dimensional accuracy.&& |
| Product Description | |
|---|---|
| Generic | PA 11 |
| Material Status | Commercial: Active |
| Features | Ductility,Renewable resources,Solvent resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | 180320 |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Apparent density | 0.48 | g/cm³ | ASTM D1895 |
| Particle size | 50.0 | µm | ASTM D3451 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| XY direction | 1800 | MPa | |
| ZX direction | 1800 | MPa | |
| tensile strength | |||
| XY direction, fracture | 50.0 | MPa | |
| ZX direction, fracture | 50.0 | MPa | |
| Tensile strain | |||
| fracture | 50 | % | ASTM D638 |
| Bending modulus | |||
| XY direction | 1600 | MPa | |
| ZX direction | 1600 | MPa | |
| bending strength | |||
| XY direction, 5% strain | 60.0 | MPa | |
| ZX direction, 5% strain | 60.0 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 6.00 | kJ/m² | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| ZX direction: 0.45 MPa, unannealed | 183 | ℃ | |
| ZX direction: 1.8 MPa, unannealed | 50.0 | ℃ | |
| Melting temperature | |||
| DSC | 202 | ℃ | ASTM D3418 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Recyclability（Refresh ratio for stable performance） | 30 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. of parts |
| 3. Powder |
| 4. Type V, 2.0 in/min |
| 5. 0.53 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |