| About |
|---|
| Produce strong, functional, detailed complex parts Robust thermoplastic produces high-density parts with balanced property profiles and strong structures. Provides excellent chemical resistance to oils, greases, aliphatic hydrocarbons, and alkalies. Ideal for complex assemblies, housings, enclosures, and watertight applications. Biocompatibility certifications – meets USP Class I-VI and US FDA guidance for Intact Skin Surface Devices. Quality at the lowest cost per part Achieve the lowest cost per part and reduce your total cost of ownership. Minimize waste – reuse surplus powder batch after batch and get functional parts, no throwing away anymore. Get consistent performance while achieving 80% surplus powder reusability. Optimize cost and part quality – cost-efficient material with industry-leading surplus powder reusability. Engineered for HP Multi Jet Fusion technology Designed for production of functional parts across a variety of industries. Provides the best balance between performance and reusability. Achieves watertight properties without any additional post-processing. Engineered to produce final parts and functional prototypes with fine detail and dimensional accuracy.&& |
| Product Description | |
|---|---|
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Biocompatible,Solvent resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | 180320 |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.01 | g/cm³ | ASTM D792 |
| Apparent density | 0.43 | g/cm³ | ASTM D1895 |
| Particle size | 60.0 | µm | ASTM D3451 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| XY direction | 1700 | MPa | |
| ZX direction | 1800 | MPa | |
| tensile strength | |||
| XY direction, fracture | 48.0 | MPa | |
| ZX direction, fracture | 48.0 | MPa | |
| Tensile strain | |||
| XY direction, fracture | 20 | % | |
| ZX direction, fracture | 15 | % | |
| Bending modulus | |||
| XY direction | 1730 | MPa | |
| ZX direction | 1730 | MPa | |
| bending strength | |||
| XY direction, 5% strain | 65.0 | MPa | |
| ZX direction, 5% strain | 70.0 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 3.50 | kJ/m² | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| XY direction: 0.45 MPa, not annealed | 175 | ℃ | |
| ZX direction: 0.45 MPa, unannealed | 175 | ℃ | |
| XY direction: 1.8 MPa, unannealed | 95.0 | ℃ | |
| ZX direction: 1.8 MPa, unannealed | 106 | ℃ | |
| Melting temperature | |||
| DSC | 187 | ℃ | ASTM D3418 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Recyclability（Refresh ratio for stable performance） | 20 | % |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. of parts |
| 3. Powder |
| 4. Type V, 2,0 in/min |
| 5. 0,53 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |