| About |
|---|
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Process Methods | Extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 300℃，1.2kg | 10±1 | g/10min | GB/T 3682.1-2008 |
| Density | 1200 | kg/m³ | GB/T 3682.1-2008 |
| Viscous average molecular weight (Mv) | 20500 | g/mol | GB/T 36214.2-2018 |
| Forming shrinkage rate | 0.6 – 0.8 | % | GB/T 39818-2021 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ≥60 | MPa | GB/T 1040.1-2018 |
| elongation at break | ≥105 | % | GB/T 1040.1-2018 |
| bending strength | ≥95 | MPa | GB/T 9341-2008 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ≥65 | KJ/m² | GB/T 1043.2-2018 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8MPa | ≥123 | ℃ | GB/T 1634.2-2019 |
| Vicat Softening Temp | ≥140 | ℃ | GB/T 1633-2000 |
| Glass transition temperature | ≥147 | ℃ | GB/T 19466.2-2004 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 1mm | 89 | % | GB/T 2410-2008 |
| b | |||
| 2mm | 0.1 – 0.5 | GB/T 39822-2021 | |
| YI | 0 – 1 | ||
| 2mm | GB/T 39822-2021 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 27 | % | GB/T 2406.1-2008 |
| Flame retardant level | V-2 | GB/T 2408-2021 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |