| About |
|---|
| EP127 is an injection molding Nylon 66 resin. This resin offers a well-balanced combination of engineering properties characterized by good toughness; high impact; good surface lubricity: abrasion resistance; self-extinguishment. Typical Applications As an injection molding resin, EP127 is suitable for the production of cable ties and other molding product.&& |
| Product Description | |
|---|---|
| Supplier | Huafon |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Self-extinguishing,Good wear resistance,V-2 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 275℃，2.16kg | 70 | g/10min | ISO 1133 |
| water content | < 4000 | ppm | Internal Method |
| Particle size | 1.40 to 2.00 | g/100 pellets | Internal Method |
| Relative viscosity | 2.62 to 2.72 | Internal Method | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 74.6 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 69 | % | ISO 527-2 |
| Bending modulus | 2640 | MPa | ISO 178 |
| bending strength | 97.6 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 184 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 66.1 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B120 | 239 | ℃ | ISO 306/B120 |
| Melting peak temperature | 267 | ℃ | ASTM D3418 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | V-2 | UL 94 | |
| 1.60 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 48h/23°C/50%RH |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |