| About |
|---|
| EP158 is a general purpose Nylon 66 resin. This resin offers a well-balanced combination of engineering properties characterized by high strength: good toughness; high impact; good surface lubricity: abrasion resistance; resistant low temperature: self-extinguishment. Typical Applications EP158 is suitable for compounding and injection molding, also widely used in spinning monofilament, staple. Terminal applications mainly in machinery, electronics, electrical, instrumentation, automotive components, railway, home appliances, communications, textile, oil pipe/tank and precision engineering products, etc., EP158 also can be used for the production of film, packing, medical equipment, sporting goods, and daily necessities and so on.&& |
| Product Description | |
|---|---|
| Supplier | Huafon |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,High impact resistance,Antifreeze,Self-extinguishing,Good wear resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13-1.14 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| 23℃，24hr | 0.04 | % | ISO 62 |
| Melt Flow Rate | |||
| 275℃，2.16kg | 70 | g/10min | ISO 1133 |
| Terminal amino group | 41±5 | Meq/Kg-NH 2 | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 75 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 70 | % | ISO 527-2 |
| bending strength | |||
| 23℃ | 98 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 2580 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 186 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 68 | ℃ | ISO 75-2/Af |
| Melting temperature | 263 | ℃ | ISO 11357-3 |
| Vicat Softening Temp | |||
| A120 | 240 | ℃ | ISO 306/A50 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.00mm | V-2 | UL 94 | |
| 3.00mm | V-2 | UL 94 | |
| 0.70mm | V-2 | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.1 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 48h/23°C/50%RH |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |