| About |
|---|
| T26P is light middle viscosity of co-polymerization. Typical Applications T26P can be used for spinning fine denier staple fibre, mainly for the production of high-grade cashmere imitation, wool fabrics and other staple fibre products.&& |
| Product Description | |
|---|---|
| Supplier | Huafon |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 | g/cm³ | Internal Method |
| water content | Internal Method | ||
| Dry chip | < 800 | ppm | Internal Method |
| Wet chip | < 5000 | ppm | Internal Method |
| Particle size | 1.70 to 2.30 | g/100 pellets | Internal Method |
| Relative viscosity | Internal Method | ||
| Dry chip | 2.62 to 2.70 | Internal Method | |
| Wet Chips | 2.58 to 2.66 | Internal Method | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 260 | ℃ | ASTM D3418 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |