| About |
|---|
| HYDEX® 4101 & 4101L (lubricated) is a very stable chemical compound that can withstand high impact without deterioration. It is approved for direct contact with food by the FDA and is ideal for machined parts in food processing equipment. HYDEX™ 4101 has excellent resistance to typical cleaning chemicals such as chlorine and caustic solutions and has a very low moisture absorption rate, as much as 15 times less than nylon. HYDEX® 4101 & 4101L (lubricated) exhibits a broad range of outstanding properties for a variety of applications, especially in the food processing industry. It is ideal for applications such as cams, bearings, gears, food pistons, wear strips, scraper blades, valve bodies and conveyor components. Good chemical resistance properties High impact strength A wear factor up to 50% better then PET-P Very low moisture absorption rate Excellent machining qualities No center line porosity&& |
| Product Description | |
|---|---|
| Supplier | Ensinger |
| Generic | 热塑性聚酯 |
| Material Status | Commercial: Active |
| Features | High impact resistance,Machinable,Food contact compliance,Good stability,Good wear resistance,Solvent resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 23℃，24hr | 0.020 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 37 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 154 | ℃ | |
| 1.8 MPa, unannealed | 93.3 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 1.1E-4 | 1/℃ | ASTM D696 |
| Operating temperature | |||
| long-term | 105 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Pressure limiting speed | 6000 | psi·fpm |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 87 | ASTM D785 | |
| Tensile modulus | |||
| 23℃ | 2960 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃ | 64.8 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 6.0 | % | |
| Fracture, 23 ℃ | 50 | % | |
| Bending modulus | |||
| 23℃ | 2960 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 89.6 | MPa | ASTM D790 |
| Compression modulus | 2170 | MPa | ASTM D695 |
| compressive strength | |||
| 10% strain, 23 ℃ | 79.3 | MPa | ASTM D695 |
| friction coefficient | |||
| dynamic | 0.25 | ||
| static state | 0.19 | ||
| Wear factor | 420 | 10^-8 mm³/N·m | ASTM D3702 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 40 PSI, 50 FPM |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |