HYDEX® 4101L - SOLIAO

About
HYDEX® 4101 & 4101L (lubricated) is a very stable chemical compound that can withstand high impact without deterioration. It is approved for direct contact with food by the FDA and is ideal for machined parts in food processing equipment. HYDEX™ 4101 has excellent resistance to typical cleaning chemicals such as chlorine and caustic solutions and has a very low moisture absorption rate, as much as 15 times less than nylon. HYDEX® 4101 & 4101L (lubricated) exhibits a broad range of outstanding properties for a variety of applications, especially in the food processing industry. It is ideal for applications such as cams, bearings, gears, food pistons, wear strips, scraper blades, valve bodies and conveyor components. Good chemical resistance properties High impact strength A wear factor up to 50% better then PET-P Very low moisture absorption rate Excellent machining qualities No center line porosity&&

About

HYDEX® 4101 & 4101L (lubricated) is a very stable chemical compound that can withstand high impact without deterioration. It is approved for direct contact with food by the FDA and is ideal for machined parts in food processing equipment. HYDEX™ 4101 has excellent resistance to typical cleaning chemicals such as chlorine and caustic solutions and has a very low moisture absorption rate, as much as 15 times less than nylon. HYDEX® 4101 & 4101L (lubricated) exhibits a broad range of outstanding properties for a variety of applications, especially in the food processing industry. It is ideal for applications such as cams, bearings, gears, food pistons, wear strips, scraper blades, valve bodies and conveyor components. Good chemical resistance properties High impact strength A wear factor up to 50% better then PET-P Very low moisture absorption rate Excellent machining qualities No center line porosity&&

Product Description
Supplier	Ensinger
Generic	热塑性聚酯
Material Status	Commercial: Active
Features	High impact resistance,Machinable,Food contact compliance,Lubricating,Good stability,Solvent resistance,Low moisture absorption
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.36	g/cm³	ASTM D792
Water absorption rate
24hr	0.070	%	ASTM D570

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2620	MPa	ASTM D638
tensile strength
fracture	49.6	MPa	ASTM D638
Tensile strain
fracture	40	%	ASTM D638
Bending modulus
23℃	2690	MPa	ASTM D790
friction coefficient			Internal Method
Steel – Dynamic	0.11		Internal Method
Steel – Static	0.080		Internal Method
Wear factor	77	10^-8 mm³/N·m	Internal Method

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	37	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	90.6	℃	ASTM D648
Continuous use temperature	105	℃	UL 746B

Supplementary information	Nominal value	Unit	Test method
Pressure limiting speed
@ 100 fpm	15700	psi·fpm

Notes
1. Typical properties: these are not to be construed as specifications.
2. 40 PSI, 50 FPM
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.