| About |
|---|
| HyFlexP021 polymer is a modified co-polyester that exhibits elastomeric properties. HyFlexP021 can be melt spun into Fiber and Monofilament, and can also be extruded for other applications that require elastic properties in the final product. HyFlexP021 co-polyester needs to be dried to <50ppm moisture (110°C/-40°C d.pt. air/14+ hours) if processed on single screw extruder. Drying in dry nitrogen atmosphere is preferred.&& |
| Product Description | |
|---|---|
| Generic | PCTG |
| Material Status | Commercial: Active |
| Features | Food contact compliance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Color b（Hunter Colorimeter） | 14.0 to 28.0 | ||
| Color L（Hunter Colorimeter） | 64.0 to 78.0 | ||
| Intrinsic viscosity | |||
| 0.1% cresol solution | 1.0 to 1.4 | ||
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 260 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | < 240 | ℃ | DSC |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 23 ℃ | 43 | ASTM D2240 | |
| tensile strength | |||
| fracture | 18.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 460 | % | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.1% Solution in M-cresol |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |