| About |
|---|
| Hyflon® MFA® is a unique family of perfluoro polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame resistance, low surface energy and exceptional dielectric properties. Hyflon® MFA® F1540 is a medium-high melt flow rate multi purpose resin with an exceptional stress crack resistance, continuous service temperature up to 225°C and a 13-15 x 10³ cycles flex-life (on a 0.3 mm film, ASTM D2176).&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | 全氟聚合物 |
| Material Status | Commercial: Active |
| Features | High liquidity,Flame Characteristics,High ESCR,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.10 to 2.15 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 372℃，5.0kg | 8.0 to 18 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 265 to 275 | ℃ | ASTM D3307 |
| Crystallization peak temperature | |||
| DSC | 255 to 265 | ℃ | DSC |
| Linear coefficient of thermal expansion | |||
| MD | 1.2E-4 to 2.0E-4 | 1/℃ | ASTM D696 |
| specific heat | |||
| 23℃ | 900 to 1100 | J/kg/℃ | DSC |
| Thermal conductivity coefficient | |||
| 40℃ | 0.20 | W/m/K | ASTM C177 |
| Crystallization heat | 16.0 to 24.0 | J/g | DSC |
| Fusion heat | 16.0 to 24.0 | J/g | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+17 | ohms | ASTM D257 |
| Volume resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric strength | |||
| 1 mm | 35 to 40 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 23 ℃，50 Hz | 2.00 | ASTM D150 | |
| 23 ℃，100 kHz | 2.00 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 23℃，50 Hz | < 5.0E-4 | ASTM D150 | |
| 23℃，100 kHz | < 5.0E-4 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | 95 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 55 to 60 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃ | 400 to 500 | MPa | ASTM D3307 |
| tensile strength | |||
| Fracture, 23 ℃ | > 25.0 | MPa | ASTM D3307 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 300 | % | ASTM D3307 |
| Bending life | 4.0E+4 to 6.0E+4 | Cycles | ASTM D2176 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 240 to 290 | °C | |
| Barrel 2 zone temperature | 270 to 320 | °C | |
| Barrel 3 zone temperature | 300 to 360 | °C | |
| Barrel 4 zone temperature | 330 to 380 | °C | |
| Barrel 5 zone temperature | 340 to 390 | °C | |
| Flange temperature | 370 to 400 | °C | |
| Connector temperature | 370 to 400 | °C | |
| Cross head temperature | 380 to 410 | °C | |
| Melt temperature | 390 to 420 | °C | |
| Nozzle temperature | 390 to 420 | °C | |
| Steel wire preheating | 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 3. 2.0 in/min |
| 4. 0.3 mm film |
| 5. 50 Hz |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |