Hyflon® PFA P120X

About
Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance, inherent flame resistance, low surface energy, and exceptional dielectric properties. Hyflon® PFA resins have been designed to retain their properties over a wide range of temperatures from cryogenic up to 300°C (572°F)* and are the material of choice in applications such as linings in the Chemical Process Industry, specialty cables, semiconductor industry, aerospace, and other challenging industries. Hyflon® PFA P120X is a low melt flow rate resin designed for blow molding applications, where very high viscosity and melt strength are needed. It also has significantly lower permeability to gasses than standard PFAs. Hyflon® PFA P12OX is an ASTM D3307 – Type XVI resin. * For rating at 300°C (572°F) contact your Solvay Representative.&&

About

Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resistance, inherent flame resistance, low surface energy, and exceptional dielectric properties. Hyflon® PFA resins have been designed to retain their properties over a wide range of temperatures from cryogenic up to 300°C (572°F)* and are the material of choice in applications such as linings in the Chemical Process Industry, specialty cables, semiconductor industry, aerospace, and other challenging industries. Hyflon® PFA P120X is a low melt flow rate resin designed for blow molding applications, where very high viscosity and melt strength are needed. It also has significantly lower permeability to gasses than standard PFAs. Hyflon® PFA P12OX is an ASTM D3307 – Type XVI resin. * For rating at 300°C (572°F) contact your Solvay Representative.&&

Product Description
Supplier	Solvay
Generic	PFA
Material Status	Commercial: Active
Features	Low liquidity,Flame Characteristics,High Heat Resistance,Hypocrystalline
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Melt Flow Rate
372℃，5.0kg	2.5 to 5.0	g/10min	ASTM D1238
Density	2.120 to 2.170	g/cm³	ASTM D792

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
280℃	49.0	MPa	ASTM D1708
23℃	500 to 600	MPa	ASTM D1708
tensile strength
Fracture, 280 ℃	4.60	MPa	ASTM D1708
Fracture, 23 ℃	> 26.0	MPa	ASTM D1708
Tensile strain
Fracture, 280 ℃	480	%	ASTM D1708
Fracture, 23 ℃	> 300	%	ASTM D1708

THERMAL	Nominal value	Unit	Test method
Melting temperature	310 to 316	℃	ASTM D3307
Crystallization peak temperature
DSC	295	℃	DSC
specific heat
23℃	0.900 to 1.10	J/kg/℃	DSC
Thermal conductivity coefficient
40℃	0.20	W/m/K	ASTM C177
Crystallization heat	35.0 to 45.0	J/g	DSC
Fusion heat	34.0 to 45.0	J/g	DSC
Linear coefficient of thermal expansion	1.2E-4 to 2.0E-4	cm/cm/℃	ASTM D696

Notes
1. Typical properties: these are not to be construed as specifications.
2. 0.039 in/min
3. 1mm/min
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.