| About |
|---|
| Nylon 66, Impact Modified&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| friction coefficient | ASTM D1894 | ||
| &Metal – Dynamic | 0.23 | ||
| With oneself – dynamic | 0.75 | ||
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 12 | µm | |
| Secant modulus | ASTM D882 | ||
| MD：12 µm | 2760 | MPa | |
| TD：12 µm | 2760 | MPa | |
| tensile strength | ASTM D882 | ||
| MD, fracture | 262 | MPa | |
| TD, fracture | 262 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 75 | % | |
| TD, fracture | 75 | % | |
| Oxygen permeability | |||
| 25℃ | 1.6 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water vapor transmittance | |||
| 12 µm，38℃，100% RH | 380 | g·mm/m²/atm/24 hr | ASTM F1249 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20° | 160 to 180 | ASTM D2457 | |
| Haze | |||
| 11.9 µm | 2.0 to 3.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |