| About |
|---|
| Product Description | |
|---|---|
| Supplier | Hyosung |
| Material Status | Commercial: Active |
| Features | High Heat Resistance |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | |||
| yield | 63 | MPa | ASTM D638 |
| yield | 63 | MPa | ISO 527-1 |
| Tensile modulus | |||
| 1,650 | MPa | ASTM D638 | |
| 1,550 | MPa | ISO 527-1 | |
| Flexural strength | |||
| 61 | MPa | ASTM D790 | |
| 61 | MPa | ISO 178 | |
| Bending modulus | |||
| 1,550 | MPa | ASTM D790 | |
| 1,450 | MPa | ISO 178 | |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| elongation | |||
| Yield tension | 20 | % | ASTM D-638 |
| Yield tension | 20 | % | ISO 527-1 |
| Breaking and stretching | 100 | % | ASTM D-638 |
| Breaking and stretching | 100 | % | ISO 527-1 |
| proportion | |||
| 1.24 | g/cm³ | ASTM D792 | |
| 1.24 | g/cm³ | ISO 1183 | |
| hardness | |||
| Coast D | ASTM D2240 | ||
| Coast D | 78 | ISO 868 | |
| Water absorption balance | |||
| At 50% RH | 0.5 | % | ASTM D570 |
| At 50% RH | 0.5 | % | ISO 62 |
| Water absorption rate | |||
| At saturation | 2.1 | % | ASTM D570 |
| At saturation | 2.1 | % | ISO 62 |
| Melt index | |||
| 240℃/2.16kg | 200 | g/10min | ASTM D1238 |
| 240℃/2.16kg | 196 | g/10min | ISO 1133 |
| Mold shrinkage rate | |||
| MD, 3mm | 1.8 | % | ASTM D-955 |
| TD, 3mm | 1.7 | % | ASTM D-955 |
| MD, 2mm | 1.5 | % | ASTM D-955 |
| TD, 2mm | 1.4 | % | ASTM D-955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| Unscratched | N.B. | ISO 179/1eA | |
| Charpy impact strength | |||
| 23 ℃ for scratches | 6 | KJ/m² | ISO 179/1eA |
| -10 ℃ for scratches | 2 | KJ/m² | ISO 179/1eA |
| -30 ℃ for scratches | 2 | KJ/m² | ISO 179/1eA |
| Izod notched impact strength | |||
| Unscratched | N.B. | ASTM D-256 | |
| Unscratched | N.B. | ISO 180/U | |
| Impact strength of cantilever beam notch | |||
| 23℃ | |||
| 60 | J/m | ASTM D256 | |
| 6 | KJ/m² | ISO 180/1A | |
| -10℃ | |||
| 45 | J/m | ASTM D256 | |
| 3 | KJ/m² | ISO 180/1A | |
| -30℃ | |||
| 30 | J/m | ASTM D256 | |
| 2 | KJ/m² | ISO 180/1A | |
| Dart impact strength | 2 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Chain breaking temperature | |||
| 222 | ℃ | ASTM D3418 | |
| 222 | ℃ | ISO 11357 | |
| Linear coefficient of thermal expansion | |||
| 25℃-55℃ | E-4 | ASTM E831 | |
| Vicat Softening Temp | |||
| 5 kg | 195 | ℃ | ASTM D1525 |
| 50 N | 190 | ℃ | ISO 306/B 50 |
| Thermal deflection temperature | |||
| 66psi | 200 | ℃ | ASTM D648 |
| 264psi | 105 | ℃ | ASTM D648 |
| 0.45 MPa | 190 | ℃ | ISO 75 |
| 1.8 MPa | 92 | ℃ | ISO 75 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| Short term 3 mm | 15 | kV/mm | ASTM D149 |
| Short term 2 mm | 19 | kV/mm | ASTM D149 |
| Volume resistivity | E-14 | ohms·cm | ASTM D257 |
| Surface resistivity | E-17 | ohm/sq. | ASTM D257 |
| Dielectric constant | |||
| At 60Hz | 6 | ASTM D150 | |
| Dissipation factor | |||
| At 60Hz | 0.012 | ASTM D150 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |