| About |
|---|
| HYSOL® ES1301™ is a silica filled epoxy casting system recommended for coils, transformers, and general pupose casting.&& |
| Product Description | |
|---|---|
| Supplier | Henkel |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Baking |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.44 | g/cm³ | |
| Shrinkage rate | |||
| MD | 0.84 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 112 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | |||
| 40 to 60 ℃ | 6.7E-5 | cm/cm/℃ | |
| 130 to 150 ℃ | 1.7E-4 | cm/cm/℃ | |
| Thermal conductivity coefficient | 0.42 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| — | 1.2E+16 | ohms | |
| — | 2.0E+14 | ohms | |
| Volume resistivity | |||
| 25 ℃ | 1.9E+16 | ohms·cm | |
| 105 ℃ | 1.4E+14 | ohms·cm | |
| Dielectric strength | |||
| 0.254 mm | 43 | kV/mm | |
| Dielectric constant | |||
| 25 ℃，100 Hz | 3.63 | ||
| 25 ℃，1 kHz | 3.62 | ||
| 25 ℃，100 kHz | 3.57 | ||
| 105 ℃，100 Hz | 4.50 | ||
| 105 ℃，1 kHz | 4.18 | ||
| 105 ℃，100 kHz | 3.90 | ||
| Dissipation factor | |||
| 25℃，100 Hz | 5.0E-3 | ||
| 25℃，1 kHz | 4.0E-3 | ||
| 25℃，100 kHz | 8.0E-3 | ||
| 105℃，100 Hz | 0.068 | ||
| 105℃，1 kHz | 0.039 | ||
| 105℃，100 kHz | 0.016 | ||
| Arc resistance | 139 | sec |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| breakdown voltage | |||
| 25℃ | 21800 | V |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| colour | |||
| — | Amber | ||
| — | Black | ||
| Weight Mix Ratio (PBW) | |||
| Part A | 100 | ||
| Part B | 38 | ||
| Volume Mixing Ratio (PBV) | |||
| Part A | 2.0 | ||
| Part B | 1.0 | ||
| Density | |||
| 25℃ | 1.19 | g/cm³ | |
| 25℃ | 1.60 | g/cm³ | |
| viscosity | |||
| Brookfield RVF, 25 ℃ | 0.75 | Pa·s | |
| Brookfield RVF, 25 ℃ | 1.6 | Pa·s | |
| Brookfield RVF, 25 ℃ | 11 | Pa·s | |
| Curing time | |||
| 110℃ | 4.0 | hr | |
| Gelation time | |||
| 25℃ | > 4.8E+2 | min |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 90 to 95 | ||
| tensile strength | 47.9 | MPa | |
| Tensile strain | |||
| fracture | 1.0 | % | |
| bending strength | 109 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Alpha 2 |
| 3. Alpha 1 |
| 4. 105°C |
| 5. 25°C |
| 6. Part B |
| 7. Part A |
| 8. Part B, Spindle 5, speed 20 rpm |
| 9. Mixed, Spindle 3, speed 20 rpm |
| 10. Part A, Spindle 5, speed 20 rpm |
| 11. 200 g mass |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |