| HYSOL® ES1900™ is a transparent, medium-viscosity epoxy resin formulation recommended for small potting and laminating applications where clarity and excellent structural, mechanical and electrical properties are required. This two-part adhesive exhibits good wetting, cures at room temperature and develops strong, low shrinkage bonds to most materials including optical fibers, glass ceramics, most metals and many rigid plastics. It has excellent dimensional stability over a wide temperature range. Fully cured, it is a durable electrical insulator with good physical properties, and excellent chemical resistance. This product is typically used in applications with an operating range of -60°C to +125°C.&& |
| Product Description | |
|---|---|
| Supplier | Henkel |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Good Electrical Properties,Low contractility,Solvent resistance,Insulation,Room Temperature Cure |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Water absorption rate | |||
| 24hr | 0.30 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 80.0 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | |||
| < 80℃ | 6.8E-5 | cm/cm/℃ | |
| > 80℃ | 1.9E-4 | cm/cm/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 3.0E+16 | ohms | |
| Volume resistivity | |||
| 25 ℃ | 3.0E+16 | ohms·cm | |
| Dielectric strength | 65 | kV/mm | |
| Dielectric constant | |||
| 25 ℃，1 kHz | 4.00 | ||
| Dissipation factor | |||
| 25℃，1 kHz | 9.0E-3 |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Weight Mix Ratio (PBW) | |||
| Part A | 100 | ||
| Part B | 46 | ||
| Volume Mixing Ratio (PBV) | |||
| Part A | 2.0 | ||
| Part B | 1.0 | ||
| Density | |||
| 25℃ | 1.06 | g/cm³ | |
| — | 1.12 | g/cm³ | |
| 25℃ | 1.15 | g/cm³ | |
| viscosity | |||
| 25℃ | 3.0 | Pa·s | |
| 25℃ | 6.0 | Pa·s | |
| 25℃ | 8.4 | Pa·s | |
| Curing time | |||
| 25℃ | 12 to 24 | hr | |
| Gelation time | |||
| 25℃ | 12 to 15 | min | |
| storage stability | |||
| 25 ℃ | 8.0 to 10 | min |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 90 | ||
| tensile strength | 68.3 | MPa | |
| Tensile strain | |||
| fracture | 6.0 | % | |
| bending strength | 100 | MPa | |
| compressive strength | 131 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Alpha 1 |
| 3. Alpha 2 |
| 4. 25°C |
| 5. Part B |
| 6. Mixed |
| 7. Part A |
| 8. 100 g mass |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |