| About |
|---|
| HYSOL® ES2202™ is an unfilled epoxy system with a high operating temperature and long pot life. It is recommended for use where excellent chemical resistance, high heat distortion temperature and good electrical properties under high humidity conditions are required. This product is recommended for servo stators, high temperature resistors, transformers, and high temperature cast shapes.&& |
| Product Description | |
|---|---|
| Supplier | Henkel |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Good Electrical Properties,Baking,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | |||
| MD | 0.70 | % | |
| Water absorption rate | |||
| 24hr | 0.11 | % | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 140 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD：< 140℃ | 6.5E-5 | 1/℃ | |
| Thermal conductivity coefficient | 0.19 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| — | 8.0E+16 | ohms | |
| — | 4.0E+15 | ohms | |
| — | 1.0E+14 | ohms | |
| Volume resistivity | |||
| 25 ℃ | 1.0E+17 | ohms·cm | |
| 85 ℃ | 4.0E+14 | ohms·cm | |
| 130 ℃ | 1.0E+14 | ohms·cm | |
| Dielectric strength | |||
| 0.254 mm | 65 | kV/mm | |
| Dielectric constant | |||
| 25 ℃，100 Hz | 4.30 | ||
| 25 ℃，1 kHz | 4.30 | ||
| 25 ℃，10 kHz | 4.20 | ||
| 25 ℃，100 kHz | 4.00 | ||
| 85 ℃，100 Hz | 4.40 | ||
| 85 ℃，1 kHz | 4.40 | ||
| 85 ℃，10 kHz | 4.40 | ||
| 85 ℃，100 kHz | 4.30 | ||
| 130 ℃，100 Hz | 4.40 | ||
| 130 ℃，1 kHz | 4.40 | ||
| 130 ℃，10 kHz | 4.40 | ||
| 130 ℃，100 kHz | 4.40 | ||
| Dissipation factor | |||
| 25℃，100 Hz | 5.0E-3 | ||
| 25℃，1 kHz | 9.0E-3 | ||
| 25℃，10 kHz | 0.022 | ||
| 25℃，100 kHz | 0.033 | ||
| 85℃，100 Hz | 2.0E-3 | ||
| 85℃，1 kHz | 3.0E-3 | ||
| 85℃，10 kHz | 4.0E-3 | ||
| 85℃，100 kHz | 9.0E-3 | ||
| 130℃，100 Hz | 3.0E-3 | ||
| 130℃，1 kHz | 3.0E-3 | ||
| 130℃，10 kHz | 3.0E-3 | ||
| 130℃，100 kHz | 2.0E-3 | ||
| Arc resistance | 110 | sec |
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Weight Mix Ratio (PBW) | |||
| Part A | 100 | ||
| Part B | 25 | ||
| Volume Mixing Ratio (PBV) | |||
| Part B | 28 | ||
| Density | |||
| 25℃ | 0.998 to 1.05 | g/cm³ | |
| 25℃ | 1.16 | g/cm³ | |
| viscosity | |||
| Brookfield RVF, 25 ℃ | 0.45 to 0.65 | Pa·s | |
| 25℃ | 8.0 to 12 | Pa·s | |
| Brookfield RVF, 25 ℃ | 11 to 14 | Pa·s | |
| Gelation time | |||
| 121℃ | 20 to 30 | min | |
| 40℃ | 2.4E+2 to 3.0E+2 | min | |
| 100℃ | 3.3E+3 to 3.9E+3 | min | |
| storage stability | |||
| 25 ℃ | 420 to 480 | min |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 80 to 85 | ||
| tensile strength | 55.2 to 68.9 | MPa | |
| bending strength | 103 to 138 | MPa | |
| compressive strength | 138 to 172 | MPa |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Alpha 1 |
| 3. 130°C |
| 4. 85°C |
| 5. 25°C |
| 6. Part B |
| 7. Part A |
| 8. Part B, Spindle 2, speed 20 rpm |
| 9. Part A, Spindle 5, speed 10 rpm |
| 10. 10 g mass |
| 11. 200 g mass |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |