| About |
|---|
| 65 Shore D Polyester Elastomer with Heat Ageing Protection Developed for Extrusion&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Features | Good heat aging resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | ISO 868 | ||
| Shaw’s D | 65 | ISO 868 | |
| Shore D, 15 seconds | 60 | ISO 868 | |
| Tensile modulus | 350 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| fracture | 44.0 | MPa | ISO 527-2 |
| yield | 21.0 | MPa | ISO 527-2 |
| 5% strain | 12.0 | MPa | ISO 527-2 |
| 10% strain | 17.8 | MPa | ISO 527-2 |
| 50% strain | 20.0 | MPa | ISO 527-2 |
| 100% strain | 23.0 | MPa | ISO 527-2 |
| 300% strain | 32.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 300 | % | ISO 527-2 |
| yield | 30 | % | ISO 527-2 |
| Tensile Creep Modulus（1 hr） | 310 | MPa | ISO 899-1 |
| Tensile creep modulus | |||
| 1000 hr | 260 | MPa | ISO 899-1 |
| Bending modulus | 374 | MPa | ISO 178 |
| abrasion resistance | 110 | mm³ | ISO 4649 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | |||
| MD | 180 | kN/m | ISO 34-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40℃ | 8.5 | kJ/m² | ISO 179/1eA |
| -30℃ | 12 | kJ/m² | ISO 179/1eA |
| 23 ℃, localized fracture | 130 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -50℃ | 10 | kJ/m² | ISO 180-1A |
| 23℃ | No Break | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -70.0 | ℃ | ISO 974 |
| Melting temperature | 211 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 1 mm | < 100 | mm/min | ISO 3795 |
| FMVSS flame retardant rating | B | FMVSS 302 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 5.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 5.00 | cm³/10min | ISO 1133 |
| Melt density | 1.06 | g/cm³ | |
| Specific Heat Capacity of Melt | 2090 | J/kg/℃ | |
| Thermal Conductivity of Melt | 0.16 | W/m/K |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 110 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.080 | % | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Melt Temperature, Optimum | 240 | °C | |
| Mold temperature | 45 to 55 | °C | |
| Mold Temperature, Optimum | 45 | °C | |
| Drying Recommended | yes | ||
| Recommended maximum moisture content | 0.060 | % | |
| Extrusion Melt Temperature, Optimum | 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 3. FMVSS 302 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |