| 55 Shore D, Renewably Sourced, High Viscosity Polyester Elastomer with Good Heat Ageing Protection Developed for Blow Molding&& |
| Product Description | |
|---|---|
| Supplier | DuPont |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Features | Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| elastic body | Nominal value | Unit | Test method |
| tear strength | |||
| MD | 140 | kN/m | ISO 34-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40℃ | 45 | kJ/m² | |
| -30 ℃, localized fracture | 160 | kJ/m² | |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 | ||
| Tensile impact strength | |||
| 23℃ | 500 | kJ/m² | ISO 8256/1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -70.0 | ℃ | ISO 974 |
| Glass transition temperature | -30.0 | ℃ | ISO 11357-2 |
| Melting temperature | 190 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 1.8E-4 | 1/℃ | |
| TD | 1.9E-4 | 1/℃ |
| Flammability level | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | IEC 60695-11-10, -20 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 50 | ISO 868 | |
| Tensile modulus | 150 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| fracture | 35.0 | MPa | |
| 5% strain | 6.40 | MPa | |
| 10% strain | 10.0 | MPa | |
| 50% strain | 16.0 | MPa | |
| 100% strain | 21.0 | MPa | |
| Tensile strain | |||
| fracture | > 300 | % | ISO 527-2 |
| Tensile creep modulus | ISO 899-1 | ||
| 1 hr | 140 | MPa | |
| 1000 hr | 90.0 | MPa |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，10.0kg | 6.0 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，10 kg | 6.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.9 | % | |
| MD | 1.4 | % | |
| Water absorption rate | ISO 62 | ||
| 23℃，24hr，2.00 mm | 0.50 | % | |
| Equilibrium, 23 ℃, 50% RH, 2.00 mm | 0.20 | % | |
| Melt density | 1.00 | g/cm³ | |
| Specific Heat Capacity of Melt | 2100 | J/kg/℃ | |
| Thermal Conductivity of Melt | 0.15 | W/m/K |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |