| About |
|---|
| Hyundai EP PA66 LD381* is a Polyamide 66 (Nylon 66) product filled with 38% glassmineral. It is available in Asia Pacific. Typical application: Automotive. Characteristics include: Good Aesthetics Heat Stabilizer Weather Resistant&& |
| Product Description | |
|---|---|
| Supplier | HYUNDAI EP |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good surface appearance,Heat Stabilized |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ASTM D1505 |
| Shrinkage rate | |||
| MD | 0.30 to 0.60 | % | ASTM D955 |
| Ash Content | 38 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 44 | J/m | ASTM D256 |
| 23℃ | 64 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 240 | ℃ | ASTM D648 |
| Melting temperature | 265 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+13 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 3.5 | kV/mm | ASTM D149 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 121 | ASTM D785 | |
| tensile strength | |||
| yield | 123 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 5.0 | % | ASTM D638 |
| Bending modulus | 6860 | MPa | ASTM D790 |
| bending strength | 216 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |