Hyundai EP TOP COAT ET509B/8902

About
ET509B is a black, high-density polyethylene produced with Sclairtech technology. It is well modified by melt blending to meet the requirements of globla standards and standards of customers’ own. It is designed for use as a top-coat in 3-layer pipe coating systems with conventional grafted adhesive (Polyglue LE149V, LE200T, LE100A and LE851P etc). Base PE of ET509B has high physical properties originated from HDPE and blended resins improve ESCR, impact properties and processibility. Together with Polyglue grades for 3-layer PE, ET509B shows highly adjusted pipe coating system available for all pipe coating specification including DIN30670, CSA Z425.21-02, NFA 49-710.&&

About

ET509B is a black, high-density polyethylene produced with Sclairtech technology. It is well modified by melt blending to meet the requirements of globla standards and standards of customers’ own. It is designed for use as a top-coat in 3-layer pipe coating systems with conventional grafted adhesive (Polyglue LE149V, LE200T, LE100A and LE851P etc). Base PE of ET509B has high physical properties originated from HDPE and blended resins improve ESCR, impact properties and processibility. Together with Polyglue grades for 3-layer PE, ET509B shows highly adjusted pipe coating system available for all pipe coating specification including DIN30670, CSA Z425.21-02, NFA 49-710.&&

Product Description
Supplier	HYUNDAI EP
Generic	PE
Material Status	Commercial: Active
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.950 to 0.970	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	0.27 to 0.36	g/10min	ASTM D1238
Water absorption rate
24hr	< 0.010	%	ASTM D570
ESCR(Environmental Stress Cracking Resistance)
10% non-ionic detergent, F50	> 1000	hr	ASTM D1693
Carbon black content	> 2.0	%	ASTM D1603

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -70.0	℃	ASTM D746
Vicat Softening Temp	> 118	℃	ASTM D1525

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	> 55		ASTM D2240
tensile strength
fracture	> 25.5	MPa	ASTM D638
Tensile strain
fracture	650	%	ASTM D638

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.