| ICORENE® 2910 is an ethylene based octene plastomer powder specifically developed for rotational moulding. This grade is designed for use in applications requiring a very flexible material.&& |
| Product Description | |
|---|---|
| Generic | 乙烯基辛烯塑料 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,Ultra high toughness,Octene copolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.882 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 10 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | > 1000 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Falling impact resistance | |||
| -20℃ | 180 | J/cm | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 46.0 | ℃ | ISO 306/A |
| Melting temperature | 75.0 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s A | 84 | ISO 868 | |
| Shaw’s D | 23 | ISO 868 | |
| tensile strength | |||
| fracture | 13.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 1000 | % | ISO 527-2 |
| Bending modulus | 24.0 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Based on ISO 6603 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |