| Braskem Idealis500 is the only High Molecular Weight Polyethylene resin in powder form specially designed for the compression molding process. Applications: Applications range from food handling cutting boards and playground toys to technical parts.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | High molecular weight |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.952 | g/cm³ | ASTM D792 |
| Apparent density | 0.45 | g/cm³ | ASTM D1895 |
| Melt Flow Rate | |||
| 190℃，21.6kg | 0.70 | g/10min | ASTM D1238 |
| Intrinsic viscosity | 4.7 | dl/g | ASTM D4020 |
| Average molecular weight | 550000 | g/mol | |
| Average particle size | |||
| Dp50 | 200 | µm | ASTM D1921 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | > 50 | kJ/m² | ISO 11542-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 80.0 | ℃ | ASTM D1525 4 |
| Melting peak temperature | 136 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 63 | ASTM D2240 | |
| tensile strength | ASTM D638 , ISO 527-2 | ||
| yield | > 20.0 | MPa | ASTM D638 , ISO 527-2 |
| fracture | > 30.0 | MPa | ASTM D638 , ISO 527-2 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | 930 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Double-notched specimens, 14° v-notch on both sides |
| 3. Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |