| About |
|---|
| Idemitsu PS NS-050 is a High Impact Polystyrene product. It can be processed by extrusion or injection molding and is available in Asia Pacific. Typical application: Housings. Characteristics include: Flame Rated Flame Retardant Good Aesthetics&& |
| Product Description | |
|---|---|
| Supplier | Idemitsu |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Good surface appearance,Flame Characteristics,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 7.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 23.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 40 | % | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 69 | J/m | ASTM D256 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 2.00 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 70 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Barrel rear temperature | 180 to 210 | °C | |
| Barrel middle temperature | 190 to 220 | °C | |
| Barrel front temperature | 210 to 240 | °C | |
| Nozzle temperature | 200 to 230 | °C | |
| Mold temperature | 40 to 60 | °C | |
| Drying temperature | 70 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Barrel 1 zone temperature | 160 to 200 | °C | |
| Barrel 2 zone temperature | 180 to 220 | °C | |
| Barrel 3 zone temperature | 200 to 240 | °C | |
| Barrel 4 zone temperature | 200 to 240 | °C | |
| Nozzle temperature | 190 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |