| PRODUCT SERIES: Rosite 3000 SERIES BMC PRODUCT DESCRIPTION: HIGH STRENGTH UL YELLOW CARD These high strength BMC composites are suitable for use in electrical applications requiring materials that possesses dielectric properties and flammability performance from UL94 HB, V-0 & 5VA. These materials can be found in Underwriters Laboratory file E53587.&& |
| Product Description | |
|---|---|
| Generic | 热固性聚酯 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Flame Characteristics,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.94 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.10 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 34.5 | MPa | ASTM D638 |
| Bending modulus | 10300 | MPa | ASTM D790 |
| bending strength | 114 | MPa | ASTM D790 |
| compressive strength | 138 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 320 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 204 | ℃ | ASTM D648 |
| Continuous use temperature | 149 | ℃ | ASTM D794 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 2.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 12 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 60 Hz | 5.15 to 5.35 | ASTM D150 | |
| 1 MHz | 4.80 to 5.00 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 1 kHz | 0.017 to 0.019 | ASTM D150 | |
| 1 MHz | 0.010 to 0.012 | ASTM D150 | |
| Arc resistance | 180 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |