| 30% CARBON FIBER REINFORCED, ELECTRICALLY CONDUCTIVE POLYPROPYLENE&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Conductive |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 310 | MPa | ASTM D638 |
| Bending modulus | 12400 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 48 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | 110 | J/m | ASTM D256 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 10 to 1.0E+4 | ohms | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 77 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 193 to 227 | °C | |
| Mold temperature | 38 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.013 to 0.025 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |