| About |
|---|
| B30G730 is a Polyethylene EBA Copolymer for Blown film Benefits & Features B30G730 is an Ethylene Butyl Acrylate (EBA) copolymer, containing 17% butyl acrylate. Applications B30G730 has been developed to give a strong and elastic film with low gel levels for applications such as Stretch hoods Surface protecton film Soft film for gloves&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | EBA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High elastic,Low speed solidification point |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.926 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ISO 1184 | ||
| 1% secant, MD: 60 µ m, blow molded film | 50.0 | MPa | ISO 1184 |
| 1% secant, TD: 60 µ m, blow molded film | 50.0 | MPa | ISO 1184 |
| tensile strength | ISO 1184 | ||
| MD, yield, 60 µ m, blow molded film | 6.00 | MPa | ISO 1184 |
| TD, yield, 60 µ m, blow molded film | 4.00 | MPa | ISO 1184 |
| MD, fracture, 60 µ m | 23.0 | MPa | ISO 1184 |
| TD, fracture, 60 µ m | 21.0 | MPa | ISO 1184 |
| Tensile strain | ISO 1184 | ||
| MD, fracture, 60 µ m | 540 | % | ISO 1184 |
| TD, fracture, 60 µ m | 680 | % | ISO 1184 |
| Drop hammer impact | 670 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 25 µ m, blow molded film | 30 | g | ASTM D1922 |
| TD: 25 µ m, blow molded film | 160 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 60 µ m, blow molded film | 40 | ASTM D2457 | |
| Haze | |||
| 60 µ m, blow molded film | 14 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |