| About |
|---|
| LDPE for Blown film 22D730 is an autoclave, low density polyethylene grade for film application. 22D730 is developed to give an extra strong film for heavy duty film applications such as sacks and pallet shrink. Applications 22D730 is intended for applications such as Heavy duty bags Shrink films Liners Construction and agricultural films&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Low density,High pressure heat resistance |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Self dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 130 | µm | |
| Secant modulus | ASTM D882A | ||
| 0.05% to 1.05%, MD: 130 µ m | 170 | MPa | |
| 0.05% to 1.05%, TD: 130 µ m | 180 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 130 µ m | 25.0 | MPa | |
| TD, yield, 130 µ m | 23.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 130 µ m | 400 | % | |
| TD, fracture, 130 µ m | 600 | % | |
| Drop hammer impact | |||
| 130 µm | 450 | g | ISO 7765-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 96.0 | ℃ | ISO 306 |
| Melting temperature | 110 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，125 µm | 43 | ASTM D2457 | |
| Haze | |||
| 125 µm | 15 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 170 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |