| LDPE for Blown film 22G764 is an autoclave, low density polyethylene grade developed to give strong film for medium duty applications. Applications 22G764 is intended for applications such as Thin shrink film Carrier-bag films Pouches and refuse sacks General packaging film&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | High anti-blocking,Inoxidizability,Low density,High pressure heat resistance |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.2 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Dynamic, blow molded film | > 0.50 | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| Elastic modulus | |||
| TD, 40 µ m, blow molded film | 200 | MPa | ASTM D882A |
| MD, 40 µ m, blow molded film | 170 | MPa | ASTM D882A |
| tensile strength | ISO 527-3 | ||
| MD, 40 µ m, blow molded film | 26.0 | MPa | ISO 527-3 |
| TD, 40 µ m, blow molded film | 23.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 300 | % | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 500 | % | ISO 527-3 |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 160 | g | ISO 7765-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 96.0 | ℃ | ISO 306 |
| Melting temperature | 110 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 40.0 µ m, blow molded film | 65 | ASTM D2457 | |
| Haze | |||
| 40 µ m, blow molded film | 8.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 190 | °C | |
| Notes |
|---|
| 1. Talc |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |