| About |
|---|
| Applications 23H430 is suitable for a variety of general-purpose packaging films, liners, carrier bags and fine shrink film. It is also recommended for cross-linked foam as well as for blow-moulding applications. Benefits and Features 23H430 is an autoclave LDPE homopolymer. It offers the following properties: Good strength and dart drop resistance Good drawdown Low tendency to block If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good dissection,Crosslinked,Foaming performance,Low density,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ISO 1183/D |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | > 0.50 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | |||
| 1% secant, 50 µ m, blow molded film | 180 | MPa | ISO 1184 |
| tensile strength | ISO 1184 | ||
| MD, yield, 50 µ m, blow molded film | 11.0 | MPa | ISO 1184 |
| TD, yield, 50 µ m, blow molded film | 12.0 | MPa | ISO 1184 |
| tensile strength | ISO 1184 | ||
| MD, fracture, 50 µ m, blow molded film | 22.0 | MPa | ISO 1184 |
| TD, fracture, 50 µ m, blow molded film | 20.0 | MPa | ISO 1184 |
| Tensile strain | ISO 1184 | ||
| MD, fracture, 50 µ m, blow molded film | 250 | % | ISO 1184 |
| TD, fracture, 50 µ m, blow molded film | 550 | % | ISO 1184 |
| Drop hammer impact | |||
| 50 µ m, blow molded film | 140 | g | ASTM D1709-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 95.0 | ℃ | ISO 306/A |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, blow molded film | 55 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | 10 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 185 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |